Leaded brass rod

ASTM B453 round bar and leaded brass bar supplier in India

Leaded brass rod specifications

Leaded brass rod specifications

Lead brass round bar size Leaded brass alloy hex bar size UNS C31200 leaded brass flat bar size
Diameter : 3mm – 800 mm 2-100 mm
  • Thickness: 2 – 100 mm
  • Width: 10 – 500 mm
Melting point UNS C33500 angle bars legth C34200 square bar size
  • 1570-1790 °F
2 to 6 meters / 8 to 20 feet 8 to120 mm
Features Fatigue strength leaded brass bars standards
  • Good strength
  • High corrosion resistance
  • Excellent wear resistance
  • 175 MPa
  • UNS C31200
  • UNS C33500
  • UNS C34000
  • UNS C34200
  • UNS C34000
  • UNS C35000
  • UNS C35300
  • UNS C35600
  • ASTM B453
  • C836
  • C857
Tensile strength Elongation Heat treatment
445 MPa
  • 25 %
  • Annealed
  • Solution Annealed
ASTM B453 bars shape Tolerances UNS C31200 leaded brass round bars condition
  • rectangular
  • hollow
  • round
  • square
  • hexagonal
  • H8
  • H9
  • H10
  • H11
  • H12
  • H13
  • K9
  • K10
  • K11
  • K12 or custom
  • Hardened & tempered
  • annealed
  • Precipitation hardened.
Most prevalent designs of ASTM B453 rod Manufacturing technique
  • Leaded brass round bar
  • leaded brass bar
  • UNS C31200 leaded brass flat bar
  • ASTM B453 hex bars
  • ASTM B453 C34000 square bars
  • ASME SB453 rectangular bars
  • UNS C34200 bright bars
  • lead brass alloy rounds
  • ASTM B453 shaft
  • leaded brass alloy billet
  • UNS C35300 bloom
  • leaded brass alloy bar stock
  • ASTM B453 C34000 polished bars
  • Lead brass alloy cold drawn bars
  • C35600 leaded brass alloy bright drawn round bars
  • UNS C33500 cold finished round bars
  • ASTM B453 hot rolled bars
  • leaded brass alloy annealed bars
  • lead brass forged round bars
  • Rolled
  • Forged

lead brass round bar

lead brass round bar

UNS C31200 leaded brass flat bar

UNS C31200 leaded brass flat bar

UNS C33500 hex bar

UNS C33500 hex bar

Searching for leaded brass alloy hex bar in rolled and forged production method? Manufacturer of wide stock UNS C31200 leaded brass flat bar

Lead brass alloy bar price

Thickness Price in AED Price in USD
6 X 2000 MM AED 69.53 US $ 18.93
3.5 X 2000 MM AED 40.73 US $ 11.09
2 X 2000 MM AED 107.54 US $ 29.28
1.5 X 2000 MM AED 95.60 US $ 26.03
8 X 2000 MM AED 52.78 US $ 14.37
12.0 X 2000 MM AED 64.13 US $ 17.46
5 X 2000 MM AED 71.88 US $ 19.57

Finding for ISO 9001 certified UNS C33500 hexagonal bar in Mumbai? We offer excellent cutting performance and stability for ASTM B453 square bar

ASTM B453 round bar grain sizes

UNS No. Temper Grain size, milimeter
Nominal Max Min
C34200/C33500/ C35000/C34000 OS070 .070 .100 .050
OS050 .050 .070 .035
OS035 .035 .050 .025
OS025 .025 .035 .015
Stockist of leaded brass alloy rod size range from 2 to 95 mm in India, we provide C34000 hollow bar UT and bend test before dispatch

Types of ASME SB453 rod

ASTM B453 leaded brass bar

ASTM B453 leaded brass bar

ASME SB453 C34000 hexagonal bar

ASME SB453 C34000 hexagonal bar

UNS C35000 square bar

UNS C35000 square bar

UNS C35300 rectangle bar

UNS C35300 rectangle bar

leaded brass alloy bright bar

leaded brass alloy bright bar

UNS C35600 forged bar

UNS C35600 forged bar

Call us to get UNS C35300 rectangle bar in hairline, mirror and polished surface finish

UNS C31200 leaded brass square bar tolerances

Temper Temper Tensile Strength
min (ksi)
Elongation
%
Rockwell B
1/2 Hard H02 57 7
1/2 Hard H02 50 15
Soft Anneal O60 40 30
1/4 Hard H01 42 20 40
1/2 Hard H02 55 10 60
1/4 Hard H01 50 10
Soft Anneal O60 44 25
1/4 Hard H01 50 15 55
Soft Anneal O60 46 20

Leaded brass bar application

Leaded brass bar application

UNS C35300 flat bar benifitis

  • Good cutting performance
  • Excellent mechanical properties
  • Suitable for cold and hot pressure processing
  • Excellent straightness and dimensional accuracy

ASTM B453 square bar chemical composition

Grade Zinc/ Zn Lead/ Pb Copper/ Cu Tin/ Sn Iron/ Fe Phosphorous/ P Nickel/ Ni
C35350 31.3 – 36.2 2.0 – 4.5 61 – 63 0.3 0.4 0.05 – 0.20 0.05 – 0.30

Lead brass alloy square bar mechanical properties

Grade Temper Fatigue Str. Tensile Str. Elong.
C35350 350 MPa /50 ksi
H02 175 MPa /25 ksi 445 MPa /64 ksi 25 %
480 MPa /69 ksi

Leaded brass rectangle bar physical properties

Melting Point – Solidus Melting Point – Liquidus Specific Gravity Density Modulus of Elasticity Thermal Conductivity Electrical Conductivity Specific Heat Capacity Coefficient of Thermal Expansion Modulus of Rigidity
°F °F lb/cu in. at 68°F ksi Btu/ sq ft/ ft hr/ °F at 68°F % IACS at 68°F Btu/ lb /°F at 68°F 68-57210 to -6 power per °F (68 – 572°F) ksi
1630 1670 8.47 0.306 15000 67 26 0.09 11.3 5600

UNS C35300 hex bar fabrication material

Technique Suitability
Brazing Good
Soldering Excellent
Gas Shielded Arc Welding
Coated Metal Arc Welding
Oxyacetylene Welding
Seam Weld
Spot Weld
Capacity for Being Cold Worked Fair
Buttweld Fair
Machinability Rating 90
Capacity for Being Hot Formed Poor